In this research the Oxide Dispersion Strengthened (ODS) Steel alloy 14 YWT with composition Fe- 14 Cr – 3 W – 0.4 Ti – 0.25 Y2O3 was... Show moreIn this research the Oxide Dispersion Strengthened (ODS) Steel alloy 14 YWT with composition Fe- 14 Cr – 3 W – 0.4 Ti – 0.25 Y2O3 was consolidated using liquid phase sintering method and it’s mechanical properties were tested and compared with standard materials. Initially the standard composition was prepared by mechanical alloying and cold compacted in to compression samples and then sintered. The consolidated sample density was determined and their compression tests were performed at various temperatures. To improve the strength aluminum powder was added into the mechanically alloyed samples via milling for 15 minutes with the aim to enhance diffusion by liquefying at higher temperatures. Initially specimens with different weight percentage of aluminum were prepared and it was discovered that 2.5% aluminum addition gave the best results; further testing was carried out at this alloy composition. The tests were carried out for 2 different post sintering processes. Tests were also carried out with copper as the sintering agent. A significant increase in yield strength with the addition of 2.5% Al and 10% cold working was observed. M.S. in Material Science, December 2011 Show less