The growing demand for nuclear energy places a high importance on the development of new materials capable of withstanding higher temperatures... Show moreThe growing demand for nuclear energy places a high importance on the development of new materials capable of withstanding higher temperatures and harsher irradiation conditions than those used in existing reactors. By supporting the development of next generation reactors it also becomes possible to close the nuclear fuel cycle, greatly reducing the amount of waste sent for disposal in deep geologic repositories, where its interaction with the environment is also a matter of interest. In this thesis, X-ray absorption fine structure (XAFS) spectroscopy is used to investigate the local atomic structure of systems of interest to nuclear energy. First, two XAFS studies on environmental materials are presented. Granular activated carbon (GAC) was treated with iron to improve its water remediation properties, specifically with respect to arsenic. XAFS was used to determine the nature of iron coating on the GAC surface, and the method of arsenic bonding to the treated surface. Next, a neodymium precipitate from solubility studies carried out for the Waste Isolation Pilot Plant (WIPP) was analyzed. Neodymium was used as an analog for plutonium in brine solutions. XAFS fitting indicated that the neodymium substituted for calcium in a gypsum lattice, providing information useful for future geochemical modeling. XAFS was also used to study radiation damage in materials. A candidate material for advanced reactor structural materials, modified 9Cr–1Mo, was irradiated to 1, 4, and 10 displacements per atom (dpa). XAFS analyses were performed on the Fe, Mo, and Nb K-edges. Irradiation caused a reduction in coordination for all three elements, but the exact behavior was element specific. Damage around Fe atoms was linear with dose, while damage around xxii Mo atoms saturated at or before 1 dpa. XAFS was shown to provide a useful atomic level description of radiation damage for a complex alloy system. Finally, zirconium carbide and zirconium nitride, candidate materials for advanced fuel claddings were studied at the Zr K-edge. Samples irradiated to 1 dpa retained overall crystallinity, as indicated by transmission electron microscopy (TEM) images but were found to have an increase in dislocation loops compared to their non-irradiated counterparts. XAFS analysis was able to determine the size of the undefected regions, making it a valuable complement to other analysis techniques. xxiii PH.D in Physics, December 2012 Show less