Exposure of graphite targets to high intensity proton beams at neutrino production facilities causes changes in the target material that can... Show moreExposure of graphite targets to high intensity proton beams at neutrino production facilities causes changes in the target material that can result in a shortened operation lifetime. The dominant factors in this process are currently thought to be mechanical in nature resulting primarily from microstructural effects that lead to thermal and structural changes in bulk material properties. As currently planned beam facilities with increased proton energy and intensity begin to come online it will be important to thoroughly understand these processes, and ideally to be able to predict the effects of new beam designs on target properties. Direct analysis of targets exposed to existing high-energy proton beams is complicated by several factors, such as very limited access to proton beam facilities, high associated costs, irradiation times on the order of months, and the resulting radioactivity of irradiated samples that requires special facilities for post-irradiation examination. Much of the existing literature concerning irradiation damage in graphite has been focused on the needs of the nuclear engineering community, however high-energy proton targets operate in a much different environment. In comparison to graphite irradiated in a nuclear reactor, graphite used in proton beam targets receives a higher dose rate, have greater gas production, and experience short irradiation pulses as opposed to continuous irradiation. Low-energy ion irradiation offers a method of inducing similar levels of radiation damage to high-energy protons while avoiding many of the difficulties and limitations associated with high-energy proton beams and the corresponding activated specimen testing. My research described in this thesis focused on investigating how low-energy ion irradiation could be used to induce the same or similar types of microstructural alteration and mechanical property degradation as that seen in high-energy neutrino production target graphites by varying damage levels and irradiation temperatures prior to post-irradiation characterization. Show less