Structural Studies of Degradation Mechanism of Lithium Rich Manganese, Nickel, and Iron Based Cathodes

Creator

Aryal, Shankar

Date

2018

Description

Layered oxide compounds are superior with respect to discharge voltage and discharge specific capacity compared to other families of cathodes....
Show moreLayered oxide compounds are superior with respect to discharge voltage and discharge specific capacity compared to other families of cathodes. Therefore, LiCoO2 and LiMnxNiyCozO2, are the most commonly used cathodes since the commercialization of lithium ion battery. Recently, Li rich Ni, Mn, and Co oxide composite cathodes have been introduced with some improvements. As Co is toxic and expensive, attempts have been made to replace Co with cheap and environmentally friendly Fe. This dissertation reports that comparable discharge specific capacity and discharge voltage can be achieved by replacing Co with Fe and optimizing the composition of Mn, Ni, and Fe. However, the capacity and voltage fading on cycling are still remaining challenges. Structural change on electrochemical cycling is the main reason behind this fading. X-ray absorption spectroscopy (XAS), the specific element probe technique to study local structure and X-ray diffraction (XRD) to study the crystallographic phase information are utilized to understand the degradation/aging mechanism. A series of Li rich Mn, Ni, and Fe oxide composite cathode materials Li1.2Mn(0.30+x)Ni(0.40-x)Fe0.10O2 for x = 0, 0.05, 0.10, 0.15, 0.20 and 0.25 were prepared using a sol-gel synthesis method. Rhombohedral and monoclinic crystal phases are found in Li rich Mn, Ni, and Fe composite oxide materials, but pure rhombohedral phase cannot be obtained without excess Li in the stoichiometric LiMO2 form. The pure monoclinic phase Li2MnO3 is also synthesized to confirm its presence in the composite oxide cathodes. Particle size and surface morphology are studied with scanning electron microscopy. The composite cathodes are cycled to over 100 cycles at 0.3C, for C = 250 mAhg-1 rate. XAS before and after 100 electrochemical cycles of Li rich Mn-Ni-Fe based cathodes is reported for the first time. The determination of fractional contents of monoclinic and rhombohedral phases in the composite oxide cathodes is not possible by powder XRD analysis, however, Li2MnO3 content decreases on decreasing Mn content and on increasing Ni content. The composition with higher Ni content has a higher degree of cation mixing. The synergistic effect of rhombohedral and monoclinic phases in Li rich Mn, Ni, and Fe based cathode is critical for stable electrochemical performance. The Li1.2Mn0.50Ni0.20Fe0.10O2 cathode showed the most stable cyclability performance (194 mAhg-1 first discharge capacity with 94 % capacity retention after 100 cycles at 0.3C rate) however, Li1.2Mn0.40Ni0.30Fe0.10O2 (220 mAhg-1 first discharge capacity with 57 % capacity retention) and Li1.2Mn0.55Ni0.15Fe0.10O2 (241 mAhg-1 first discharge capacity with 68 % capacity retention) cathodes showed higher 1st discharge capacity but poor cyclability under the same charge/discharge cycling.The XAS at Mn K-edge is used to explain the mechanism of Li2MnO3 activation for the improved electrochemical performance of Li rich Mn, Ni, and Fe oxide composite cathode, however Li2MnO3 contributed differently in different compositions. Synchrotron XRD and XAS measurements probed the lattice size expansion, which decreases the chemical potential of Li ions in the cathode on cycling leading to lower discharge voltage after cycling.
Show less